| PROPERTY | UNIT | VALUE / RANGE |
| Melting Point | °C | 327 - 346 |
| Density | g mL-1 | 1.80 - 2.41 |
| Coefficient of Thermal Expansion x 10-5 | cm / (cm °C) | 9.6 - 9.9 |
| Heat Deflection Temperature, 0.5 MPa | °C | |
| Heat Deflection Temperature, 1.8 MPa | °C | |
| Thermal Conductivity | W / mK | 0.1 - 0.92 |
| Shore Hardness, D Scale | n/a | D55 - D70 |
| PROPERTY | UNIT | VALUE / RANGE |
| Tensile Strength, Yield at 23 C | MPa | 12.4 - 13.7 |
| Tensile Strength, Break at 23 C | MPa | 26 - 35 |
| Elongation, Yield | % | 325 |
| Elongation, Break | % | 250 - 580 |
| Tensile Modulus at 23 C | MPa | 480 - 630 |
| Flexural Strength, Yield | MPa | |
| Flexural Modulus | MPa | 490 |
| Compressive Strength | MPa | |
| Izod Notched | J / m | |
| Izod Unnotched | J / m | 185 |
| PROPERTY | UNIT | VALUE / RANGE | |
| Ohm-cm | ||
| Dielectric Strength | V/mm x 104 | 6 - 7 | |
| Dielectric Constant @ 1 MHz | n/a | 2.02 - 2.1 | |
| Dissipation Factor @ 1 MHz | n/a, x 10-4 | 0.3 - 0.7 |
| PROPERTY | UNIT | VALUE / RANGE | |
| °C | ||
| Mold Shrinkage | % | ||
| Continuous Service Temperature | °C | 260 | |
| Water Absorption, 24 hr. Immersion | % | 0 - 0.02 |